Eryone High Speed ABS Green 1.75mm 1kg – Ultra-Fast, Industrial-Grade ABS Filament

Eryone High Speed ABS Green 1.75mm 1kg – Ultra-Fast, Industrial-Grade ABS Filament

ERYONE Hyper-Speed ABS Filament

Engineered for speed, strength, and industrial reliability

ERYONE Hyper-Speed ABS is a next-generation ABS filament specifically formulated for high-speed 3D printing without compromising part strength or dimensional stability. By optimizing material flow characteristics, this filament enables significantly faster print speeds while minimizing internal stress and shrinkage, resulting in stable, accurate prints even on demanding geometries.

The Eryone High Speed ABS Blue 1.75mm 1kg filament is designed for users who need fast print speeds without sacrificing strength or heat resistance. Unlike standard ABS, Eryone High Speed ABS Blue 1.75mm 1kg offers improved flow, reduced warping, and excellent layer bonding for functional 3D printed parts.

Compared to standard ABS and PLA, Hyper-Speed ABS delivers nearly double the impact strength of PLA, making it an excellent choice for functional parts that require durability, heat resistance, and long-term performance. With a high heat distortion temperature, it performs reliably in elevated-temperature environments and is well suited for mechanical components, automotive applications, and technical enclosures.

Key Features & Benefits

• Optimised for high-speed printing up to 600 mm/s

• Reduced warping and shrinkage for improved print stability

• High impact resistance for tougher, more durable parts

• Excellent heat resistance for functional and load-bearing applications

• Designed for use in enclosed printers

Recommended Printing Settings

• Nozzle Temperature: 240 – 290 °C

• Bed Temperature: 80 – 110 °C

• Build Surface: Glass, PEI, or Spring Steel Plate

• Enclosure: Recommended (closed printing environment)

• Printing Speed: 30 – 600 mm/s

• Drying Conditions: 75 – 85 °C for 6 hours

Material Properties (Typical Values)

• Density: 1.1 g/cm³

• Heat Distortion Temperature (0.45 MPa): 95 °C

• Melt Index: 20 g/10 min

Mechanical Performance (Printed Samples)

• Tensile Strength (X-Y): 15.68 MPa

• Elastic Modulus (X-Y): 217 MPa

• Elongation at Break (X-Y): 10.16 %

• Tensile Strength (X-Z): 13.16 MPa

• Elastic Modulus (X-Z): 217 MPa

• Elongation at Break (X-Z): 5.11 %

All test samples were printed at 270 °C nozzle temperature, 100 mm/s print speed, 95 °C bed temperature, 100 % infill, and a 0.4 mm nozzle.

Ideal Applications

• Functional mechanical parts

• Automotive components

• Technical housings and brackets

• High-strength prototyping

Important Note

Material performance may vary depending on printer setup, part design, and environmental conditions. Values provided are for reference and comparison purposes only and should not be used as final design specifications.

Spool Compatibility: Supplied on a plastic spool, making it fully compatible with CFS and AMS multi-material systems for smooth, reliable filament feeding.